タイトル: | The formation of poly-Si films on flat glass substrates by flash lamp annealing |
著者: | Watanabe, Taiki Ohdaira, Keisuke |
キーワード: | Flash lamp annealing Amorphous silicon Polycrystalline silicon Crystallization Film stress |
発行日: | 2015-08-06 |
出版者: | Elsevier |
誌名: | Thin Solid Films |
巻: | 595 |
号: | Part B |
開始ページ: | 235 |
終了ページ: | 238 |
DOI: | 10.1016/j.tsf.2015.08.003 |
抄録: | We have succeeded the formation of polycrystalline silicon (poly-Si) films by flash lamp annealing (FLA) of 4-μm-thick intrinsic amorphous silicon (a-Si(i)) films deposited directly on flat glass substrates by tuning catalytic chemical vapor deposition (Cat-CVD) conditions. The use of a-Si(i) films deposited without intentional substrate heating leads to the suppression of Si film peeling during FLA. The a-Si(i) films deposited at room temperature have low film density, low film stress, and high defect density, compared to a-Si(i) films deposited at higher temperatures. The prevention of Si film peeling may be due to the low film stress and/or the suppression of the emergence of lateral explosive crystallization (EC) by using a-Si(i) films with low film density. |
Rights: | Copyright (C)2015, Elsevier. Licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International license (CC BY-NC-ND 4.0). [http://creativecommons.org/licenses/by-nc-nd/4.0/] NOTICE: This is the author's version of a work accepted for publication by Elsevier. Taiki Watanabe and Keisuke Ohdaira, Thin Solid Films, 595(Part B), 2015, 235-238, http://dx.doi.org/10.1016/j.tsf.2015.08.003 |
URI: | http://hdl.handle.net/10119/16139 |
資料タイプ: | author |
出現コレクション: | c10-1. 雑誌掲載論文 (Journal Articles)
|
このアイテムのファイル:
ファイル |
記述 |
サイズ | 形式 |
3040.pdf | | 437Kb | Adobe PDF | 見る/開く |
|
当システムに保管されているアイテムはすべて著作権により保護されています。
|