タイトル: | Comprehensive study of potential‐induced degradation in silicon heterojunction photovoltaic cell modules |
著者: | Yamaguchi, Seira Yamamoto, Chizuko Ohdaira, Keisuke Masuda, Atsushi |
キーワード: | Potential-induced degradation Photovoltaic module Silicon heterojunction solar cell Reliability Acceleration test Ionomer |
発行日: | 2018-04-16 |
出版者: | John Wiley & Sons, Ltd |
誌名: | Progress in Photovoltaics |
巻: | 26 |
号: | 9 |
開始ページ: | 697 |
終了ページ: | 708 |
DOI: | 10.1002/pip.3006 |
抄録: | Accelerated tests were used to study potential-induced degradation (PID) in photovoltaic (PV) modules fabricated from silicon heterojunction (SHJ) solar cells containing tungsten-doped indium oxide (IWO) transparent conductive films on both sides of the cells and a rear-side emitter. A negative bias of −1000 V was applied to a module with respect to the cover glass surface in a chamber maintained at 85 °C, which significantly reduced the cell’s short-circuit current density (J_<sc>) within several days. Based on dark current density–voltage and external quantum efficiency measurements, the reduction in the J_<sc> was attributed to optical losses rather than carrier recombination. X-ray absorption fine structure spectroscopy showed the formation of metallic indium (In) in the IWO layers of a degraded cell, which suggests that the root cause of the optical loss was a darkening of the front IWO layers caused by the precipitation of metallic In. In extremely severe PID tests, the SHJ PV modules exhibited not only a further reduction in the J_<sc> but also a moderate reduction in the open-circuit voltage (V_<oc>). These J_<sc> and V_<oc> reductions were probably caused by sodium being introduced into the base region of the cells. A comparison of the PID test results of the SHJ PV modules with those of other types of PV modules indicates that SHJ PV modules have a relatively high resistance to PID. As a module with an ionomer encapsulant exhibited little degradation, their high resistances to PID may be further improved by using encapsulants with high electrical resistances. |
Rights: | Copyright (C) 2018 John Wiley & Sons, Ltd. This is the pre-peer reviewed version of the following article: Seira Yamaguchi, Chizuko Yamamoto, Keisuke Ohdaira, Atsushi Masuda, Progress in Photovoltaics, 26(9), 2018, pp.697-708, which has been published in final form at http://dx.doi.org/10.1002/pip.3006. This article may be used for non-commercial purposes in accordance with Wiley Terms and Conditions for Use of Self-Archived Versions. |
URI: | http://hdl.handle.net/10119/16205 |
資料タイプ: | author |
出現コレクション: | c10-1. 雑誌掲載論文 (Journal Articles)
|
このアイテムのファイル:
ファイル |
記述 |
サイズ | 形式 |
3025.pdf | | 5237Kb | Adobe PDF | 見る/開く |
|
当システムに保管されているアイテムはすべて著作権により保護されています。
|